Gray glass composition

ABSTRACT

The present invention provides a glass composition having a neutral gray color and a luminous (visible) transmittance within a range that allows the glass to be used as privacy glazing in a vehicle. The glass of the present invention has a standard soda-lime-silica flat glass base composition and uses iron, cobalt and selenium, and optionally nickel, as the colorants. It has also been found that a nickel-free, neutral gray colored glass with a luminous transmittance (C.I.E. illuminant A) of up to 40% at a thickness of 3.9 millimeters may be attained by using as colorants: 0.59 to 0.99 wt. % of the total glass Fe 2 O 3  (total iron), no greater than 0.30 wt. % FeO; 60 to 180 PPM CoO and 5 to 30 PPM Se. It has been found that a nickel-bearing, neutral gray colored glass with a luminous transmittance (C.I.E. illuminant A) of up to but less than 40% at a thickness of 3.9 millimeters may be attained by using as colorants: 0.35 to 1.1 wt. % of the total glass Fe 2 O 3  (total iron), no greater than 0.30 wt. % FeO; 60 to 180 PPM CoO; 1 to 30 PPM Se; and 25 to 550 PPM NiO.

[0001] This is a continuation in part application of U.S. patent application Ser. No. 08/153,733, filed Nov. 16, 1993.

BACKGROUND OF THE INVENTION

[0002] This invention involves a neutral gray colored glass that has a luminous transmittance that makes it highly desirable for use as privacy glazing in vehicles, e.g. in the rear portions of vans. In particular, the glass of the present invention has a luminous transmittance range of up to 45 percent. The desired color and performance is attained by using iron, cobalt, selenium and/or nickel as colorants. In addition, the glass of the present invention generally exhibits lower infrared and total solar energy transmittance than typical green glasses used in automotive applications to reduce heat gain in the interior of the enclosure. The glass is also compatible with flat glass manufacturing methods.

[0003] Various heat-absorbing glass substrates are known in the art. The primary colorant in typical green tinted automotive glasses is iron, which is usually present in both the Fe₂O₃ and FeO forms. As is conventional, the total amount of iron present in a glass is expressed herein as Fe₂O₃, regardless of the form actually present. Typical green tinted automotive glass has about 0.5 percent by weight total iron with the ratio of FeO to total iron being about 0.25.

[0004] Some glasses, e.g. U.S. Reissue Pat. No. 25,312 to Duncan et al. and U.S. Pat. No. 4,339,541 to Dela Ruye, produce a gray color in the glass by including nickel oxide, cobalt oxide and selenium as colorants. However, inclusion of nickel-containing materials must be carefully controlled because the presence of nickel during the melting process sometimes leads to the formation of nickel sulfide stones in the glass. Additional potential problems faced when using nickel include haze formation on the glass surface due to reduction of the nickel in the tin bath and change in the glass color when it is heat treated.

[0005] To avoid this problem, nickel-free colored glasses containing iron oxide, cobalt oxide, and selenium were developed, as disclosed in U.S. Pat. No. 3,296,004 to Duncan et al., U.S. Pat. No. 3,723,142 to Kato et al. and British Pat. Specification 1,331,492 to Bamford. In U.S. Pat. No. 4,104,076 to Pons, instead of nickel, Cr₂O₃ or UO₂ are used in combination with iron oxide, cobalt oxide, and selenium to produce gray glass. More recent nickel-free gray glasses are disclosed in U.S. Pat. Nos. 5,023,210 to Krumwiede et al. and 5,278,108 to Cheng et al. and EP 536 049 to Alvarez-Casariego, et al., which use iron oxide, cobalt oxide and selenium, as colorants. Krumwiede et al. and Alvarez-Casariego et al. further disclose that chromic oxide may be used as an additional colorant.

[0006] Many of the commercially available gray glasses are too dark to be used in the forward vision area of a vehicle. In addition, the glasses may also be too dark to allow safety lighting mounted in the interior of the vehicle from being seen from the exterior of the vehicle. It would be desirable to have a neutral gray glass that provides a dark gray color for use in privacy areas of a vehicle while allowing adequate safety lighting illumination and have a consistent color and further that is compatible with commercial flat glass manufacturing techniques.

SUMMARY OF THE INVENTION

[0007] The present invention provides a glass composition having a neutral gray color and a luminous (visible) transmittance within a range that allows the glass to be used as privacy glazing in a vehicle. The glass of the present invention has a standard soda-lime-silica flat glass base composition and uses iron, cobalt and selenium, and optionally nickel, as the colorants. It has been found that a nickel-free, neutral gray colored glass with a luminous transmittance (C.I.E. illuminant A) of up to 40% at a thickness of 3.9 millimeters may be attained by using as colorants: 0.59 to 0.99 wt. % of the total glass Fe₂O₃ (total iron), no greater than 0.30 wt. % FeO; 60 to 180 PPM CoO and 5 to 30 PPM Se. In one embodiment, the glass composition includes 0.75 to 0.86 wt. % Fe₂O₃; 0.18 to 0.25 wt. % FeO; 108 to 144 PPM CoO and 13 to 24 PPM Se. It has been found that a nickel-bearing, neutral gray colored glass with a luminous transmittance (C.I.E. illuminant A) of up to but less than 45% at a thickness of 3.9 millimeters may be attained by using as colorants: 0.35 to 1.1 wt. % of the total glass Fe₂O₃ (total iron), no greater than 0.30 wt. % FeO; 60 to 180 PPM CoO; 1 to 30 PPM Se; and 25 to 550 PPM NiO. In one embodiment, the glass composition includes 0.71 to 0.94 wt. % Fe₂O₃, 0.181 to 0.24 wt. % FeO, 98 to 150 PPM CoO, 14 to 24 PPM Se, and a minimum of 50 PPM NiO.

[0008] The dominant wavelength of the glasses in the present invention may vary somewhat in accordance with particular color preferences. In the present invention, it is preferred that the glass be a neutral gray color characterized by dominant wavelengths in the range of 480 to 580 nanometers, preferably 485 to 560 nanometers, with an excitation purity of no higher than 8%, preferably no higher than 3%.

DETAILED DESCRIPTION

[0009] The base glass of the present invention, that is, the major constituents of the glass without colorants, is commercial soda-lime-silica glass characterized as follows: Weight % SiO₂ 66 to 75 Na₂O 10 to 20 CaO  5 to 15 MgO 0 to 5 Al₂O₃ 0 to 5 K₂O 0 to 5 BaO 0 to 1

[0010] To this base glass, the present invention adds colorants in the form of iron, cobalt, selenium and/or nickel. In one particular embodiment of the invention, the glass is essentially nickel-free; that is, no deliberate addition of nickel or nickel compounds is made, although the possibility of traces of nickel due to contamination may not always be avoided. The glass in the present invention is essentially free of other colorants, such as, but are not limited to chromium, manganese, cerium, molybdenum, titanium, chlorine, zinc, zirconium, sulfur, fluorine, lithium and strontium. In particular, the glass composition taught herein does not include chromium as a colorant as does several of the gray colored glasses in the prior art. It has been found the inclusion of chromium tends to reduce the luminous transmittance and total solar energy transmittance and increase the dominant wavelength of the glass. It should be appreciated that the glass compositions disclosed herein may include small amounts of the materials identified above, for example as melting and refining aids, tramp materials or impurities. It should be further appreciated that some of these materials as well as others may be added to the glass to improve the solar performance of the glass as will be discussed later in more detail.

[0011] The selenium colorant contributes a pink color to the glass as well as a brown color when complexed with iron to form iron selenide (FeSe). Cobalt produces a blue color. Iron contributes yellow and blue in varying proportions depending upon the oxidation state. Nickel, if used, contributes a green-brown to yellow-brown color.

[0012] The glass of the present invention may be melted and refined in a continuous, large-scale, commercial melting operation and formed into flat glass sheets of varying thicknesses by the float method in which the molten glass is supported on a pool of molten metal, usually tin, as it assumes a ribbon shape and is cooled. It should be appreciated that as a result of forming the glass on molten tin, measurable amounts of tin oxide may migrate into surface portions of the glass on the side that was in contact with the tin. Typically, a piece of float glass has an SnO₂ concentration of at least 0.05 wt. % in the first few microns below the surface of the glass that was in contact with the tin.

[0013] The total amount of iron present in the glass is expressed herein in terms of Fe₂O₃ in accordance with standard analytical practice, but that does not imply that all of the iron is actually in the form of Fe₂O₃. Likewise, the amount of iron in the ferrous state is reported as FeO, even though it may not actually be present in the glass as FeO. The proportion of the total iron in the ferrous state is used as a measure of the redox state of the glass and is expressed as the ratio FeO/Fe₂O₃, which is the weight percent of iron in the ferrous state (expressed as FeO) divided by the weight percent of total iron (expressed as Fe₂O₃). Unless stated otherwise, the term Fe₂O₃ in this specification shall mean total iron expressed in terms of Fe₂O₃ and the term FeO shall mean iron in the ferrous state expressed in terms of FeO.

[0014] The glass compositions disclosed in the present invention may be made using any of several types of melting arrangements, such as but not limited to, a conventional, overhead fired continuous melting operation as is well known in the art or a multi-stage melting operation, of the type that is discussed later in more detail. However, for glass compositions having a redox of less than 0.30, the former operation is preferred and for glass compositions having a redox of 0.30 or greater, the latter operation is preferred.

[0015] Conventional, overhead fired continuous melting operations are characterized by depositing batch material onto a pool of molten glass maintained within a tank type melting furnace and applying thermal energy until the materials are melted into the pool of molten glass. The melting tanks conventionally contain a large volume of molten glass so as to provide sufficient residence time for currents in the molten glass to affect some degree of homogenization and fining before the glass is discharged into a forming operation.

[0016] The multi-stage glass melting and refining operation disclosed in U.S. Pat. Nos. 4,381,934 to Kunkle et al.; 4,792,536 to Pecoraro et al.; and 4,886,539 to Cerutti et al. is characterized by separate stages whereby more flexibility in controlling redox conditions is provided. The overall melting process disclosed in these patents consists of three stages: a liquefaction stage, a dissolving stage, and a vacuum refining stage. In the liquefaction stage, batch materials, preferably in a pulverulent state, are fed into a rotating, drum-shaped liquefying vessel. As batch material is exposed to the heat within the vessel, liquefied material flows down a sloped batch material lining to a central drain opening at the bottom of the vessel. A stream of liquefied material falls freely from the liquefaction vessel into a dissolving vessel for the dissolving stage. The dissolving vessel completes the dissolution of unmelted particles in the liquefied material coming from the liquefaction stage by providing residence time at a location isolated from the downstream refining stage. The dissolving vessel may be in the form of a horizontally elongated refractory basin with the inlet and outlet at opposite ends thereof so as to assure adequate residence time. The refining stage preferably consists of a vertically upright vessel that may be generally cylindrical in configuration having an interior ceramic refractory lining shrouded in a gas-tight, water-cooled casing. As the molten material enters the vessel from the dissolving vessel, it encounters a reduced pressure within the refining vessel. Gases included in the melt expand in volume, creating a foam. As foam collapses, it is incorporated into the liquid body held in the refining vessel. Refined molten material is drained from the bottom of the refining vessel into a receiving chamber and delivered to a float forming chamber.

[0017] A stirring arrangement may be employed in the multi-stage process to homogenize the glass after it has been refined in order to produce glass of the highest optical quality. If desired, a stirring arrangement may be integrated with a float forming chamber, whereby the glass in the stirring chamber rests on a layer of molten metal. The molten metal may be continuous with the molten metal constituting the support in the forming chamber, and is usually comprised essentially of tin.

[0018] The multi-stage operation discussed above generally operates at a redox level of 0.30 or higher; however, redox levels below 0.30 may be achieved by increasing the amount of oxidizing constituents in the glass batch. For example, manganese oxide may be added to lower the redox level. Redox may also be controlled by adjusting the gas/O₂ ratio of the burners.

[0019] The transmittance data provided throughout this disclosure is based on a glass thickness of 3.9 millimeters (0.154 inch). Luminous transmittance (LT_(A)) is measured using C.I.E. 1931 standard illuminant “A” over the wavelength range 380 to 770 nanometers at 10 nanometer intervals. Total solar ultraviolet transmittance (TSUV) is measured over the wavelength range 295 to 395 nanometers at 10 nanometer intervals. Total solar infrared transmittance (TSIR) is measured over the wavelength range 775 to 2125 nanometers at 50 nanometer intervals. Total solar energy transmittance (TSET) represents a computed value based on measured transmittances from 275 to 2125 nanometers at 50 nanometer intervals. All solar transmittance data is calculated using Parry Moon air mass 2.0 solar data. Glass color in terms of dominant wavelength and excitation purity are measured using C.I.E. 1931 standard illuminant “C” with a 2° observer.

[0020] To determine this transmittance data, the transmittance values are integrated over the wavelength range [a,b]. This range is divided into n equal subintervals of length h by points {X₀, X₁, . . . , X_(n)} where X_(i)=a+(i×h). In the present disclosure, the Rectangular Rule is used to compute the transmittance data. An interpolating function is used to approximate the integrand ƒ in each subinterval. The sum of integrals of this function provides an approximation of the integral: l = ∫_(a)^(b)f(X)  X

[0021] In the case of the Rectangular Rule, a constant value ƒ(X_(i)) is used as an approximation of ƒ(X) on [X_(i−1), X_(i)]. This yields a step-function approximation of ƒ(X) on [a,b], and the numerical integration formula: $l = {\sum\limits_{l = 1}^{n}\quad {{f\left( X_{i} \right)} \times h}}$

[0022] Tables 1 and 2 illustrate examples of glass compositions at a 3.9 mm (0.154 in.) reference thickness which embody the principles of the present invention. Only the colorant portions of the examples are listed in the table below, with Fe₂O₃ being total iron, including that present as FeO.

[0023] The information provided in Examples 1 to 29 of Table 1 and Examples 41 to 68 of Table 2 are based on a computer model that generates theoretical spectral properties based on the glass compositions. The compositions in Table 1 exclude nickel oxide as a colorant while the compositions in Table 2 include nickel oxide as a colorant. In addition, the information provided in Examples 30 to 33 in Table 1 is based on experimental laboratory melts and the information for Examples 34 to 40 of Table 1 is based on actual glass produced using the multi-stage melting process discussed earlier. However, under certain conditions, it may be preferred that the glasses disclosed in the present invention be made using a conventional, overhead fired continuous melting process as discussed earlier.

[0024] It should be noted that Examples 1 to 29 in Table 1 were modeled to include up to 1 PPM NiO; 6 to 13 PPM of Cr₂O₃ and up to 46 PPM MnO₂, each of which are considered to be tramp and/or residual levels of these materials, to better reflect the expected spectral properties of the glass. The analysis of Examples 30 to 33 in Table 1 showed less than 3 PPM NiO and from 6 to 13 PPM Cr₂O₃ and the analysis of Examples 34 to 40 showed less than 3 PPM NiO and between 5 to 9 PPM Cr₂O₃. In addition, the analyses showed that Examples 35, 37, 38 and 40 included 30 up to 46 PPM MnO₂ and Examples 34, 36, and 39 included 566 PPM; 940 PPM and 1208 PPM MnO₂, respectively. Manganese was added to these later glass compositions to control redox in a manner as discussed earlier. It is believed that the level of MnO₂ in Examples 34, 36 and 39 will slightly lower LTA, TSUV and TSET and may operate as a weak colorant imparting a yellow/green color component in the glass. The modeled compositions in Table 2 included up to 13 PPM Cr₂O₃.

[0025] The representative base glass composition for the examples is as follows: SiO₂ 71 to 75% by weight Na₂O 13 to 14 CaO 8 to 9 MgO 3 to 4 Al₂O₃ 0.1 to 0.7

[0026] It should be appreciated that this composition may vary especially as a result of the actual amount of colorant present in the glass composition. TABLE 1A 1 2 3 4 5 6 7 8 9 10 Fe₂O₃ wt. % 0.59 0.59 0.59 0.60 0.60 0.60 0.65 0.65 0.65 0.70 FeO wt. % 0.156 0.156 0.156 0.159 0.159 0.153 0.172 0.172 0.172 0.185 Redox 0.265 0.265 0.265 0.265 0.265 0.255 0.265 0.265 0.265 0.265 CoO PPM 140 155 80 127 150 65 179 80 116 179 Se PPM 22 11 29 22 12 9 13 29 19 19 LT_(A) 34.23 38.13 38.61 35.77 38.12 52.43 33.46 37.97 38.31 30.20 TSIR 34.77 35.05 34.68 34.26 34.49 34.99 31.84 31.59 31.79 29.32 TSUV 24.36 30.24 21.35 24.13 29.34 26.05 27.16 20.00 24.29 22.86 TSET 36.06 39.02 36.80 36.29 38.53 43.48 35.24 34.80 36.05 31.87 DW nm 549.3c 478.3 585.0 496.1c 478.2 524.4 477.6 584.1 504.2c 475.1 Pe % 2.48 12.48 14.75 1.51 10.91 1.13 14.14 14.9 0.71 9.0

[0027] TABLE 1B 11 12 13 14 15 16 17 18 19 20 Fe₂O₃ wt. % 0.70 0.70 0.71 0.710 0.75 0.80 0.82 0.82 0.82 0.845 FeO wt. % 0.185 0.185 0.181 0.181 0.198 0.212 0.205 0209 0.209 0.211 Redox 0.265 0.265 0.255 0.255 0.265 0.265 0.25 0.255 0.255 0.25 CoO PPM 135 150 98 75 130 120 120 124 100 124 Se PPM 21 10 17 14 15 18 18 16 20 19 LT_(A) 34.30 38.24 43.63 48.81 37.59 36.78 36.39 39.28 40.42 35.43 TSIR 29.34 29.59 29.44 29.53 27.31 25.25 26.75 24.89 24.85 25.80 TSUV 22.08 27.43 20.72 21.85 23.62 21.15 18.78 18.30 17.14 18.08 TSET 33.04 35.96 36.51 38.60 33.65 31.75 32.26 32.38 32.32 31.31 DW nm 559.7c 480.0 562.5 563.0 481.1 486.2 552.0 495.0 569.1 550.4 Pe 1.39 12.48 2.7 3.88 5.25 1.11 0.52 2.39 5.41 0.51

[0028] TABLE 1C 21 22 23 24 25 26 27 28 29 30 Fe₂O₃ wt. % 0.85 0.90 0.935 0.95 0.98 0.98 0.98 0.99 1.10 0.818 FeO wt. % 0.225 0.238 0.261 0.251 0.259 0.259 0.259 0.262 0.281 0.245 Redox 0.265 0.265 0.279 0.265 0.265 0.265 0.265 0.265 0.255 0.300 CoO PPM 100 140 148 110 179 179 115 127 124 126 Se PPM 23 24 23 20 29 11 17 18 20 18 LT_(A) 36.29 30.56 27.95 35.55 24.20 31.59 36.18 34.07 34.43 32.68 TSIR 23.32 21.56 18.09 20.09 18.98 19.28 19.24 18.93 16.35 19.66 TSUV 18.22 16.90 13.21 17.46 14.05 20.12 17.98 17.42 12.17 20.86 TSET 29.88 26.81 23.58 27.94 22.71 27.21 27.94 26.94 24.95 26.75 DW nm 579.4 584.8 500.3 569.5 518.6c 481.1 498.4 491.2 551.0 488.8 Pe 6.95 1.38 0.97 2.98 1.23 15.35 1.34 2.07 3.67 2.79

[0029] TABLE 1D 31 32 33 34 35 36 37 38 39 40 Fe₂O₃ wt. % 0.826 0.93 0.935 0.657 0.803 0.811 0.816 0.817 0.822 0.825 FeO wt. % 0.257 0.257 0.261 0.190 0.212 0.212 0.186 0.215 0.216 0.236 Redox 0.313 0.276 0.279 0.289 0.264 0.261 0.228 0.264 0.263 0.286 CoO PPM 105 120 128 66 118 120 121 124 124 124 Se PPM 17 19 19 11 18 17 20 18 16 19 LT_(A) 35.83 31.95 31.19 51.83 36.15 36.56 36.38 35.93 36.13 33.84 TSIR 18.75 18.40 18.07 32.59 24.84 25.99 29.36 24.52 25.11 21.21 TSUV 21.89 16.59 17.35 32.55 22.91 22.19 21.07 22.35 22.24 21.82 TSET 27.56 25.52 25.17 42.46 31.47 32.30 33.96 31.30 31.74 28.43 DW nm 497.6 515.6 496.4 510.2 492.7 490.7 556.1 488.0 487.1 494.5 Pe 1.56 1.05 1.71 0.67 0.91 1.36 0.20 1.56 2.52 0.92

[0030] TABLE 2A 41 42 43 44 45 46 47 48 49 Fe₂O₃ wt. % 0.40 0.45 0.50 0.50 0.51 0.51 0.52 0.55 0.60 FeO wt. % 0.102 0.119 0.130 0.128 0.135 0.135 0.138 0.146 0.153 Redox 0.255 0.265 0.265 0.255 0.265 0.265 0.265 0.265 0.255 CoO PPM 102 110 135 100 115 100 179 95 110 Se PPM 6 11 12 8 12 1 15 4 10 NiO PPM 400 250 350 200 250 350 500 450 200 LT_(A) 42.21 39.78 33.25 45.52 37.88 44.16 24.68 39.97 41.74 TSIR 46.29 42.82 39.15 40.24 38.92 38.97 37.28 36.21 34.40 TSUV 36.94 35.13 32.27 31.41 32.14 39.83 29.36 35.73 26.55 TSET 45.87 43.13 38.39 43.91 40.13 43.47 33.72 39.66 38.95 DW nm 558.8 547.0 524.8 505.5 553.6 491.1 520.9 548.1 515.8 Pe % 3.55 0.53 0.45 1.34 0.81 4.86 0.26 3.06 1.29

[0031] TABLE 2B 50 51 52 53 54 55 56 57 58 Fe₂O₃ wt. % 0.60 0.65 0.70 0.71 0.71 0.75 0.80 0.82 0.82 FeO wt. % 0.153 0.172 0.185 0.181 0.181 0.198 0.212 0.209 0.209 Redox 0.255 0.265 0.265 0.255 0.255 0.265 0.265 0.255 0.255 CoO PPM 102 105 125 98 98 90 90 124 124 Se PPM 12 8 11 14 14 2 2 18 20 NiO PPM 100 250 300 100 50 450 500 200 150 LT_(A) 44.50 40.06 34.15 42.58 43.92 39.70 37.97 33.86 34.07 TSIR 36.67 31.41 28.85 29.25 29.38 26.64 24.59 24.44 24.51 TSUV 25.84 29.86 26.54 21.68 21.74 29.99 28.40 17.49 16.96 TSET 40.17 36.98 32.95 36.03 36.72 34.09 32.10 29.55 29.62 DW nm 513.6 498.6 510.2 558.9 546.2 532.0 544.8 566.3 568.7 Pe % .97 1.92 1.12 3.37 1.91 3.06 4.52 6.16 6.2

[0032] TABLE 2C 59 60 61 62 63 64 65 66 67 68 Fe₂O₃ wt. % 0.82 0.85 0.90 0.935 0.935 0.935 0.950 1.00 1.10 1.10 FeO wt. % 0.209 0.225 0.238 0.238 0.238 0.238 0.251 0.265 0.291 0.291 Redox 0.255 0.265 0.265 0.255 0.255 0.255 0.265 0.265 0.265 0.265 CoO PPM 124 135 140 170 160 150 130 110 160 100 Se PPM 20 12 15 19 19 19 10 5 12 8 NiO PPM 50 350 250 200 150 100 400 450 400 300 LT_(A) 36.25 30.23 29.83 24.48 26.21 28.06 29.90 33.06 25.07 35.01 TSIR 24.72 22.82 21.27 20.36 20.25 20.55 19.58 18.20 15.62 15.84 TSUV 17.05 22.17 19.94 13.51 13.56 13.62 20.79 21.84 25.43 18.81 TSET 30.73 27.76 26.63 23.56 24.30 25.08 25.72 26.26 21.42 25.45 DW nm 562.6 532.9 517.1 502.6 505.4 509.2 535.9 530.5 503.4 536.8 Pe % 3.27 1.82 1.12 1.62 1.40 1.22 2.72 3.40 2.75 3.54

[0033] Referring to Tables 1 and 2, the present invention provides a neutral gray colored glass using a standard soda-lime-silica glass base composition and iron, cobalt and selenium, and optionally nickel as colorants. Not all of the examples are the same gray color as indicated by the dominant wavelengths (DW) and excitation purities (Pe). In the present invention, it is preferred that the glass be a neutral gray color characterized by dominant wavelengths in the range of 480 to 580 nanometers, preferably 485 to 560 nanometers, with an excitation purity of no higher than 8%, and preferably no higher than 3%. In addition, for both the nickel-free and nickel-bearing compositions, glasses having a dominant wavelength that is a complimentary wavelength within this wavelength range may also provide the desired neutral color, especially at an excitation purity of no higher than 3% and preferably no higher than 1.5%, as shown in Examples 1, 4, 9, 11 and 23.

[0034] In the present invention, the colorants used to produce a neutral, nickel-free gray colored glass with an LT_(A) of up to 40% at a thickness of 3.9 millimeters includes 0.59 to 0.99 wt. % of the total glass Fe₂O₃ (total iron), no greater than 0.30 wt. % FeO; 60 to 180 PPM CoO and 5 to 30 PPM Se and preferably 0.71 to 0.935 wt. % Fe₂O₃; 0.181 to 0.285 wt. % FeO; 75 to 150 PPM CoO and 11 to 24 PPM Se, and more preferably 0.75 to 0.86 wt. % Fe₂O₃; 0.18 to 0.25 wt. % FeO; 108 to 144 PPM CoO and 13 to 24 PPM Se.

[0035] In the present invention, a nickel-bearing, neutral gray colored glass with a luminous transmittance of up to but less than 45% at a thickness 25 of 3.9 millimeters may be attained by using as colorants: 0.35 to 1.1 wt. % of the total glass Fe₂O₃ (total iron), no greater than 0.30 wt. % FeO; 60 to 180 PPM CoO; 1 to 30 PPM Se; and 25 to 550 PPM NiO, and preferably 0.71 to 0.94 wt. % Fe₂O₃; 0.181 to 0.24 wt. % FeO; 98 to 150 PPM CoO; 14 to 24 PPM Se, and a minimum of 50 PPM NiO.

[0036] The redox ratio for the glass of the present invention is maintained between about 0.20 to 0.30, and preferably between 0.24 to 0.28 which is the typical operating range for a conventional overhead fired melting operation. Higher redox levels may be attained by processes disclosed herein, but the use of higher redox ratios is preferably avoided to prevent excessive volatilization of selenium during melting.

[0037] Glass made by the float process typically ranges from a sheet thickness of about 1 millimeters to 10 millimeters. For the vehicle glazing applications, it is preferred that the glass sheets have a thickness within the thickness range of 1.8 to 6 millimeters.

[0038] If desired, ultraviolet radiation absorbing materials may be added to the glass compositions of the present invention to improve its solar performance. Although not limiting in the present invention, a total of up to 2.0 wt. % of oxides of cerium, vanadium, titanium and molybdenum and combinations thereof may be used as UV absorbers to reduce the TSUV of the glass. In a preferred embodiment of the invention, TiO₂ is the preferred UV absorber and may be added in an amount ranging from 0.1 to 1.0 wt. % of the glass composition, and more preferably 0.2 to 0.5 wt. %. It should be appreciated that in sufficient quantities, the cerium, vanadium, titanium and molybdenum may also operate as a colorant in the glass composition, with the cerium and titanium contributing a yellow component to the glass color, the vanadium contributing a green component to the glass color, and the molybdenum contributing a green component to the glass color.

[0039] Other variations as are known to those of skill in the art may be resorted to without departing from the scope of the invention as defined by the claims that follow. 

We claim:
 1. A neutral gray colored glass composition having a base glass portion comprising: SiO₂ 66 to 75 percent by weight Na₂O 10 to 20 CaO 5 to 15 MgO 0 to 5 Al₂O₃ 0 to 5 K₂O 0 to 5

and a colorant portion consisting essentially of: Fe₂O_(3 (total iron)) 0.6 to 0.935 percent by weight FeO up to 0.30 CoO 60 to 180 PPM Se 5 to 30 PPM

the glass having a luminous transmittance of 20 to 39.28 percent at a thickness of 3.9 millimeters.
 2. The composition as in claim 1 wherein the Fe₂O₃ concentration is from 0.71 to 0.935 weight percent, the FeO concentration is from 0.181 to 0.285 weight percent, the CoO concentration is from 75 to 150 PPM and the Se concentration is from 11 to 24 PPM.
 3. The composition of claim 1 wherein the color of the glass is characterized by dominant wavelengths in the range of 480 to 580 nanometers and an excitation purity of no higher than 8% at a thickness of 3.9 millimeters.
 4. The composition of claim 3 wherein the color of the glass is characterized by dominant wavelengths in the range of 485 to 540 nanometers and an excitation purity of no higher than 3 percent.
 5. The composition as in claim 1 further including additional ultraviolet absorbing material.
 6. The composition as in claim 5 wherein said ultraviolet absorbing material is an oxide of a material selected from a group consisting essentially of cerium, vanadium, titanium and molybdenum and combination thereof in an amount up to 2.0 wt. % of the glass composition.
 7. The composition as in claim 6 wherein said TiO₂ is in an amount from 0.1 to 1.0 wt. %.
 8. The composition as in claim 7 wherein said TiO₂ is in an amount from 0.2 to 0.5 wt. %.
 9. A glass sheet made from the composition as recited in claim 1 .
 10. The glass sheet as in claim 9 wherein the sheet has a thickness between 3 to 6 mm.
 11. The glass sheet as in claim 9 wherein the color of the glass is characterized by dominant wavelengths in the range of 480 to 580 nanometers and an excitation purity of no higher than 8% at a thickness of 3.9 millimeters.
 12. The glass sheet as in claim 11 wherein the color of the glass is characterized by dominant wavelengths in the range of 485 to 540 nanometers and an excitation purity of no higher than 3 percent.
 13. A neutral gray colored glass composition having a base glass portion comprising: SiO₂ 66 to 75 percent by weight Na₂O 10 to 20 CaO 5 to 15 MgO 0 to 5 Al₂O₃ 0 to 5 K₂O 0 to 5

and a colorant portion consisting essentially of: Fe₂O₃ (total iron) 0.6 to 1.1 percent by weight FeO up to 0.30 CoO 60 to 180 PPM Se 10 to 30 PPM NiO 25 to 550 PPM

the glass having a luminous transmittance of 20 to 44.5 percent at a thickness of 3.9 millimeters.
 14. The composition as in claim 13 wherein the Fe₂O₃ concentration is from 0.71 to 0.94 weight percent, the FeO concentration is from 0.181 to 0.24 weight percent, the CoO concentration is from 98 to 150 PPM and the Se concentration is from 14 to 24 PPM and the NiO concentration is at least 50 PPM.
 15. The composition of claim 13 wherein the color of the glass is characterized by dominant wavelengths in the range of 502 to 580 nanometers and an excitation purity of no higher than 8% at a thickness of 3.9 millimeters.
 16. The composition of claim 15 wherein the color of the glass is characterized by dominant wavelengths in the range of 502 to 540 nanometers and an excitation purity of no higher than 3 percent.
 17. The composition as in claim 13 further including additional ultraviolet absorbing material.
 18. The composition as in claim 17 wherein said ultraviolet absorbing material is an oxide of a material selected from a group consisting essentially of cerium, vanadium, titanium and molybdenum and combination thereof in an amount up to 2.0 wt. % of the glass composition.
 19. The composition as in claim 1 8 wherein said TiO₂ is in an amount from 0.1 to 1.0 wt. %.
 20. The composition as in claim 19 wherein said TiO₂ is in an amount from 0.2 to 0.5 wt. %.
 21. A glass sheet made from the composition as recited in claim 13 .
 22. The glass sheet as in claim 21 wherein the sheet has a thickness between 3 to 6 mm.
 23. The glass sheet as in claim 21 wherein the color of the glass is characterized by dominant wavelengths in the range of 502 to 580 nanometers and an excitation purity of no higher than 8% at a thickness of 3.9 millimeters.
 24. The glass sheet as in claim 23 wherein the color of the glass is characterized by dominant wavelengths in the range of 502 to 540 nanometers and an excitation purity of no higher than 3 percent.
 25. A neutral gray colored glass composition having a base glass portion comprising: SiO₂ 66 to 75 percent by weight Na₂O 10 to 20 CaO 5 to 15 MgO 0 to 5 Al₂O₃ 0 to 5 K₂O 0 to 5

and a colorant portion consisting essentially of: Fe₂O_(3 (total iron)) 0.59 to 0.99 percent by weight FeO up to 0.30 CoO 60 to 180 PPM Se 5 to 30 PPM

the glass having a luminous transmittance of up to 40 percent at a thickness of 3.9 millimeters.
 26. The composition as in claim 25 wherein the Fe₂O₃ concentration is from 0.75 to 0.86 weight percent, the FeO concentration is from 0.18 to 0.25 weight percent, the CoO concentration is from 108 to 114 PPM and the Se concentration is from 13 to 24 PPM.
 27. The composition of claim 26 wherein the color of the glass is characterized by dominant wavelengths in the range of 485 to 560 nanometers and the corresponding complementary wavelengths and an excitation purity of no higher than 8% at a thickness of 3.9 millimeters.
 28. The composition of claim 27 wherein the glass is characterized by an excitation purity of no higher than 3 percent.
 29. A neutral gray colored glass composition having a base glass portion comprising: SiO₂ 66 to 75 percent by weight Na₂O 10 to 20 CaO 5 to 15 MgO 0 to 5 Al₂O₃ 0 to 5 K₂O 0 to 5

and a colorant portion consisting essentially of: Fe₂O_(3 (total iron)) 0.35 to 1.1 percent by weight FeO up to 0.30 CoO 60 to 180 PPM Se 1 to 30 PPM NiO 25 to 550 PPM

the glass having a luminous transmittance of less than 45 percent at a thickness of 3.9 millimeters.
 30. The composition of claim 29 wherein the color of the glass is characterized by dominant wavelengths in the range of 485 to 560 nanometers and the corresponding complementary wavelengths and an excitation purity of no higher than 8% at a thickness of 3.9 millimeters.
 31. The composition of claim 30 wherein the glass is characterized by an excitation purity of no higher than 3 percent. 